Delamination Mode I Analysis on Thin Stitch Fiberglass Composite

Delamination is a major failure Mode in laminated composites, typically triggered by premature interlaminar matrix cracking and leading to severe structural degradation. To address this, various through-thickness reinforcement strategies have been explored, including three-dimensional woven architecture. Although these designs significantly improve delamination resistance, their industrial adoption stays limited due to reproducibility challenges and the high cost and operational complexity of advanced manufacturing systems needed for controlled through-thickness reinforcement. This study investigates an alternative interlaminar reinforcement method, through-thickness stitching, aimed at enhancing Mode-I delamination resistance of a commercial fiberglass laminate without changing its native architecture. Composites were manufactured using a low-viscosity epoxy infusion system (MAX 1618 A/B) and a 0/90 biaxial fiberglass fabric. An eight-filament polyethylene thread (Ø = 0.12 mm) was introduced in predefined stitch architectures consisting of three longitudinal patterns having two, three, and five continuous stitch lines, referred to as AV, BV and CV samples, respectively. Results show that stitching highly increases Mode-I interlaminar fracture toughness GIC by 0.3808, 0.4152 and 0.5192 kJ/m2 for AV, BV and CV respectively, compared to 0.0265 kJ/m2 for the unstitched composite O, highlighting the strong influence of stitch orientation and spacing on interlaminar performance. But scanning electron microscopy revealed added failure mechanisms in stitched specimens, including localized fiber misalignment of up to 33° and resin-rich regions approximately 0.6 mm in length, suggesting that while stitching enhances delamination resistance, it may also influence other mechanical properties.