This study explores how variations in mechanical alloying time and sintering temperature influence the microstructure, mechanical properties, and corrosion resistance of MnAlCuFeTi high-entropy alloys (HEAs). The MnAlCuFeTi alloy was produced by means of mechanical alloying for 5, 10, 15, and 20 h. Afterward, the alloy samples were sintered at two different temperatures: 550 °C and 650 °C. Structural properties were analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDX). Analysis of grain sizes, calculated using the Scherrer formula from SEM images, confirmed that grain size had decreased to the nanostructured regime and that microstructural homogeneity had improved. Corrosion behavior was evaluated using polarization curves, corrosion current density (Icorr), and corrosion rate measurements. The results show that increasing the mechanical alloying time reduces the alloy’s grain size, thereby improving its mechanical and corrosion resistance. At a sintering temperature of 550 °C, Icorr and corrosion rate decrease with increasing grinding time, whereas at 650 °C, although high temperatures accelerate diffusion processes and increase phase homogeneity, they weaken corrosion resistance. These findings emphasize the importance of balancing alloying time and sintering temperature to optimize performance in high-corrosion-resistant HEA applications.
Çağlar et al. (Thu,) studied this question.