Cellulose paper, a natural polymeric dielectric, determines the lifetime of oil–paper insulation systems in transformers, yet its molecular degradation behavior in ester-based insulating media remains insufficiently clarified. This study investigates the electro–thermal aging of cellulose polymer immersed in soybean-based natural ester (SBNE) and palm fatty acid ester (PFAE), with emphasis on depolymerization and its relationship with partial discharge (PD) activity. Accelerated aging experiments were conducted under combined electrical and thermal stress, and the evolution of the degree of polymerization (DP) was measured to quantify polymer chain scission. Phase-resolved PD (PRPD) patterns were recorded during aging, and multi-dimensional statistical features were extracted and reduced using principal component analysis to characterize degradation-sensitive electrical responses. The results show a progressive decrease in DP with aging time in both ester media, accompanied by distinct PD evolution characteristics, indicating different influences of the two esters on cellulose polymer stability. An ensemble learning model integrating multiple classifiers was further employed to identify aging stages based on PD features, achieving reliable discrimination performance. These findings establish a correlation between cellulose depolymerization and dielectric discharge behavior, providing a polymer-centered interpretation of aging mechanisms in ester-based oil–paper insulation systems.
Ye et al. (Sat,) studied this question.