Activated carbons are usually prepared from natural precursors (e.g., fruit stones or nutshells) by carbonization and activation processes carried out at 400–1000 °C. They exhibit well-developed porosity, and chemical activation introduces hydrophilic functional groups on their surface, providing excellent sorption properties. However, the high temperatures required during thermal treatment increase production costs. In this work, cost-reducing methods for preparing carbon sorbents are proposed. Carbonization of H3PO4 activated waste pistachio nutshells was performed using classical pyrolysis (500 or 550 °C, 30 min, N2 atmosphere) and microwave treatment (power 1000 W, 20 min). The properties of the synthesized carbons were characterized using thermogravimetry and spectroscopic techniques including infrared (ATR), Raman, photoelectron (XPS) spectroscopies, and scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM-EDS). Porous structure parameters were determined using nitrogen adsorption experiments. The efficiency of Pb2+ removal from spiked ultrapure, tap and river water was evaluated by batch sorption experiments and inductively coupled plasma–mass spectrometry. The most porous carbons were those prepared at 500 and 550 °C, with specific surface areas of 910 and 256 m2/g, respectively. Surface phosphates increased the Pb2+ sorption efficiency to 99% from ultrapure water, at an initial concentration of 300 µg Pb2+/L. The material obtained with the microwave method was not fully carbonized and remained nonporous, but it also exhibited 99% Pb2+ uptake from ultrapure water due to the presence of oxygen-containing surface groups. The Pb2+ removal from spiked tap and river water reached up to 84% and 94%, respectively, at the spiking level of 300 µg Pb2+/L.
Sobiesiak et al. (Fri,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: