This work provides a comprehensive exploration of α-olefin polymerization characteristics catalyzed by the classic α-diimine Ni catalyst. The polymerization process exhibited quasi-living behaviour, and a reaction kinetic model for the monomer coordination–insertion process was established. It was observed that the reaction exhibits living polymerization features during the first 10 min, and the coordination–insertion rate constant was determined to be 1.08 L·mol−1·s−1 at 30 °C. The regulation rules for factors including co-catalyst amount, monomer concentration, polymerization temperature, monomer type on the molecular weight, molecular weight distribution and chain structure of poly(α-olefin)s were clarified. The co-catalyst (methylaluminoxane) primarily served to activate the catalyst without inducing a chain transfer effect, suggesting that chain stagnation is likely the primary cause of the deviation from typical living polymerization behaviour. Based on temperature-controlled experiments, the activation energy for the coordination–insertion reaction was calculated to be 28.40 kJ·mol−1 through GPC curve analysis. The kinetic model established in this study, along with the revealed chain branching rules, provides a theoretical foundation for the design of poly(α-olefin)s with novel structures and functions.
Wang et al. (Wed,) studied this question.