Leaching carbon residue (LCR) is a carbonaceous solid waste generated during the hydrometallurgical recycling of spent lithium-ion batteries. Although its high graphite content offers substantial potential for resource recovery, the residual heavy metals and fluorides present in LCR pose considerable environmental risks. Currently, LCR has not garnered sufficient attention within the industry, and the lack of recycling technologies suitable for large-scale disposal results in resource wastage and environmental pollution. To address these challenges, this study proposes an innovative strategy based on the concept of multi-field synergistic enhancement. The proposed approach involves recovering and regenerating graphite (RG) from LCR via low-temperature molten salt roasting assisted by high-pressure and mechanical activation. A combination of advanced characterization techniques was employed to compare the physicochemical properties of RG and commercial graphite (CG) and to systematically evaluate the technical feasibility of using regenerated graphite as an anode material for lithium-ion batteries. The results demonstrate that, under optimized molten salt roasting and aqueous leaching conditions, the carbon content of RG reaches 99.94 wt%, indicating the efficient removal of non-carbon impurities from the graphite matrix. Compared to CG, RG retains a typical layered structure; however, a lower carbon content (99.94 wt%) and poorer structural order (ID/IG = 0.30) are observed. In terms of electrochemical performance, RG delivers a discharge specific capacity of 394.64 mAh/g during the first cycle and exhibits excellent cycling stability, with a capacity retention of 86.50% after 100 cycles. This electrochemical performance is comparable to that of commercial graphite. The proposed multi-field-assisted low-temperature molten salt roasting technique enables the efficient recovery of high-value graphite resources from LCR, establishing a full-lifecycle recycling strategy tailored for lithium-ion battery applications.
Zhang et al. (Tue,) studied this question.