Ball-end copy-milling is widely used for finishing complex components, yet its influence on surface integrity is generally overlooked and remains insufficiently addressed. Milling often generates tensile residual stresses at the machined surface, which are detrimental to fatigue performance and commonly require costly postprocessing, particularly in fatigue-critical parts such as turbine blades. In this context, the present study evaluates the capability of Prestress-Assisted Machining under uniform bending loads to improve the surface integrity of ball-end copy-milled Aluminium 5083 workpieces. Experimental tests were conducted on slender specimens with different thicknesses and curvature radii while maintaining constant cutting conditions. After machining and unclamping, surface residual stresses were measured by X-ray diffraction, and the effects of prestressing on geometry, cutting forces and surface roughness were also assessed. The results demonstrate that this method markedly increases compressive residual stresses in the prestressing direction, from approximately 30 MPa to about 180 MPa, and that this variation can be accurately described by subtracting the elastic prestressing stress from the residual stresses obtained without external loads applied. Moreover, no relevant adverse effects were observed in cutting forces or roughness, and corrected toolpaths allowed a uniform slot depth. These findings identify bending-based Prestress-Assisted Machining as an effective and predictable strategy for improving surface integrity in ball-end copy-milling and extend its applicability beyond previously reported pocket and slot milling operations.
García et al. (Wed,) studied this question.