The development of high-performance multifunctional electrodes for both supercapacitors and the oxygen evolution reaction (OER) is critical for advancing energy storage and conversion systems. Herein, a self-supported Fe-Ni 3 S 2 /FeOOH heterostructure on nickel foam (Fe-Ni 3 S 2 /FeOOH@NF) is fabricated via a combined hydrothermal-electrodeposition method. The abundant heterogeneous interfaces between crystalline Fe–Ni₃S₂ and amorphous FeOOH induce strong electronic interactions, which significantly enhance charge transfer and reaction kinetics, especially for supercapacitors. As a supercapacitor electrode, the Fe-Ni 3 S 2 /FeOOH@NF electrode delivers a high specific capacitance of 838 F g −1 at 1 A g −1 . The assembled hybrid supercapacitor device achieves a specific capacitance of 63 F g −1 and exhibits outstanding cycling stability, retaining 87.3% of its initial capacity after 10,000 cycles. Furthermore, the electrode demonstrates notable electrocatalytic performance for the OER, requiring a low overpotential of 262 mV to reach 50 mA cm −2 . These results underscore the great potential of the Fe-Ni 3 S 2 /FeOOH@NF as a high-performance, multifunctional material for advanced energy storage applications. • Crystalline Fe-Ni 3 S 2 and amorphous FeOOH heterogeneous interfaces are constructed. • The strong electronic interaction on the interfaces optimize the reaction kinetics. • The Fe-Ni 3 S 2 /FeOOH@NF electrode delivers a specific capacity of 838 F g −1 at 1 A g −1 . • The device shows a capacity retention rate of 87.3% after 10,000 cycles. • The Fe-Ni 3 S 2 /FeOOH@NF shows a low OER overpotential of 262 mV at 50 mA cm −2 .
Wang et al. (Thu,) studied this question.