Studies were conducted on the effect of the partial substitution of nickel in an LaNi5 alloy with germanium (5% by weight) or magnesium (3.3% by weight), in addition to surface modification using phosphomolybdic heteropolyacid (MPA) on the course of corrosion and passivation processes of hydrogen electrodes in a highly alkaline environment. The investigations were carried out by means of electrochemical impedance spectroscopy (EIS) and the potentiodynamic methods to analyse changes in the electrochemical parameters as a function of exposure time. The surface topography of the electrodes and chemical composition were investigated utilising a KEYENCE VHX-7000 digital microscope (Osaka, Japan) and a scanning electron microscope (SEM) equipped with an energy-dispersive spectroscopy EDS X-ray microanalysis attachment. The novelty of this work lies in the systematic, time-dependent comparison of the effects of bulk and surface modifications on the evolution of corrosion-passivation mechanisms of electrodes based on the LaNi5 alloy. It has been shown that the Mg and Ge additives improve corrosion resistance in the initial stage of exposure but lead to destabilisation of the passive layer during prolonged electrolyte interaction. A different effect was observed for the MPA-modified electrodes, in which a stable protective layer forms, limiting corrosion while maintaining favourable hydrogen desorption kinetics. The obtained results indicate the key role of exposure time (>140 h) in shaping the corrosion mechanisms and emphasise the need for simultaneous optimisation of the alloy composition and surface properties in the design of durable hydrogen electrodes.
Giza et al. (Fri,) studied this question.