Silicon carbide particle-reinforced aluminum matrix (SiCp/Al) composites are prone to surface defects during grinding owing to the heterogeneous deformation of the aluminum matrix and SiC particles, rendering conventional two-dimensional roughness parameters inadequate for precise surface characterization. In this study, three-dimensional surface roughness parameters were adopted to assess the ground surface quality of SiCp/Al composites. Orthogonal grinding experiments were carried out with four key process parameters (grinding wheel grit size, spindle speed, feed speed, and grinding depth), and the quantitative relationships between processing parameters and 3D roughness parameters, including arithmetical mean height (Sa), root mean square height (Sq), skewness (Ssk), kurtosis (Sku), surface bearing index (Sbi), core fluid retention index (Sci), and valley fluid retention index (Svi), were analyzed. The results reveal that the machined surface presents typical features including grooves from abrasive–matrix interaction, pits induced by SiC particle pull-out, scratches caused by dragged SiC particles, and tailing phenomena due to aluminum matrix melting under grinding heat. Grinding parameters exert distinct effects on surface topography: grinding wheel grit size shows the most significant influence on the Sa index, with its weight decreasing from 34% to 13% as grit becomes finer, while the combined influence weight of spindle speed, feed speed and grinding depth increases from 22% to 29%. Based on the comprehensive 3D roughness evaluation index, the optimal grinding parameter combination is determined as 320# grinding wheel, 4000 r/min spindle speed, 20 mm/min feed speed and 20 μm grinding depth. Additionally, the PSO-BP neural network achieves higher accuracy and better stability in predicting Sa and Sci than the conventional BP neural network.
Li et al. (Fri,) studied this question.