A new sulfonated diamine monomer, 9,9-bis(4-aminophenyl)fluorene-2,7-disulfonic acid (BAPFDS), was synthesized by direct sulfonation of the parent diamine, 9,9-bis(4-aminophenyl)fluorene (BAPF), using fuming sulfuric acid as the sulfonating reagent. A series of sulfonated polyimides with different sulfonation degrees were prepared from 1,4,5,8-naphthalenetetracarboxylic dianhydride (NTDA), BAPFDS, and common nonsulfonated diamines. The resulting sulfonated polyimides generally showed good solubility in m-cresol and DMSO. Proton conductivities of these polyimide membranes were measured as the functions of relative humidity and temperature. The resulting homopolyimide, NTDA-BAPFDS, displayed proton conductivities quite similar to those of Nafion 117 in the whole humidity range (RH < 100%). At 100% relative humidity, all the BAPFDS-based polyimide membranes showed proton conductivities similar to or higher than those of Nafion 117. In addition, BAPFDS-based polyimide membranes exhibited much better water stability than those derived from a widely used sulfonated diamine, 2,2‘-benzidinedisulfonic acid (BDSA), with similar IEC. This is probably because of the higher basicity of BAPFDS, which is favorable for maintaining the stability of imido rings.
Guo et al. (2002) studied this question.