An investigation was conducted of failure modes and criteria for their occurrence in composite sandwich beams. The initiation of the various failure modes depends on the material properties of the constituents (facings and core), geometric dimensions and type of loading. The beams were made of unidirectional carbon/epoxy facings and aluminum honeycomb and PVC closed-cell foam cores. The constituent materials were fully characterized and in the case of the foam core, failure envelopes were developed for general two-dimensional states of stress. Sandwich beams were loaded under bending moment and shear and failure modes were observed and compared with analytical predictions. The failure modes investigated are face sheet compressive failure, adhesive bond failure, indentation failure, core failure andfacing wrinkling.