Experimental Investigation on the Effects of POE Oil and Iron Powder on the Corrosion of TP2 Copper Tubes in Acetic Acid Vapors

The incidence of fire accidents resulting from refrigerant leaking following the rupture of air conditioning condenser tubes has escalated in recent years. Corrosion from carboxylic acid is a primary cause in the rupture of copper tubes. The influence of lubricating oil and iron filings generated by the wear of air conditioning compressors on the corrosion of condenser copper tubes is rarely mentioned in the existing research. In order to simulate the environmental conditions inside the air conditioning unit, this study utilizes acetic acid vapor to corrode copper tubes and explores the effects of lubricating oil and iron powder on copper tube corrosion. The results demonstrate that copper corrosion follows a dendritic corrosion pattern, achieving a maximum depth of 51 μm after 28 days in 1% acetic acid vapor. A small amount of copper hydroxy acetate appears in the early stage. Copper hydroxy acetic and basic carbonate copper are converted into acetic acid copper hydrate as the acetic acid vapor increases over time. The ultimate products appear as turquoise-blue crystals. POE lubricant diminishes the corrosion rate by establishing an oil layer barrier that mitigates the volatilization of acetic acid. Iron powder preferentially reacts with acetic acid to initially protect the copper tube. The Fe3+ produced oxidizes the copper in acetic acid, hence the concentration of copper acetate rises, which facilitates the crystallization of copper acetate.