Observational analysis shows increased yield strength in high-Mn steels with Al addition, highlighting improvements in toughness and embrittlement zone.
High-Mn steels are commonly fabricated by hot rolling and on-line cooling for cryogenic applications, because there exists an aging embrittlement zone in most high-Mn steels, and this shortcoming makes it difficult to optimize their mechanical properties by heat treatments. Hence, 0.6C-18Mn-0/3/5Al (in wt.%) steels were designed to investigate the effects of Al on their strength and toughness. The addition of 5 wt.% Al can increase yield strength from 357 to 461 MPa and the Charpy impact absorbed energy from 56 to 119 J. Although there is still a cryogenic aging embrittlement zone in each steel, we found that the addition of Al can narrow this brittle zone. Moreover, the absorbed energy is lowered by around 89%, 48%, and 40% for the 0Al, 3Al, and 5Al steels at −196 °C, respectively. Additionally, impact plastic deformation mechanisms were also revealed in the steels with a heat-treating temperature of 600 °C, revealing that the main deformation mechanism shifts from numerous partial dislocation slip to twinning plus strong planar slip as the addition of Al increases.
No takes yet. Share an insight, caveat, or question.
Li et al. (2025) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: