Electron beam irradiation-induced transport and recombination in p-type gallium oxide grown on (001) β-Ga2O3 substrate

This study investigates minority electron diffusion length and carrier recombination phenomena in p-type 300 nm-thick Ga2O3 films homoepitaxially grown over a (001) tin-doped β-Ga2O3 conductive substrate. This research is novel due to its systematic and near-simultaneous measurements in the top layer of a p-Ga2O3/n-Ga2O3 structure using independent electron beam-induced current and cathodoluminescence techniques. Previous work primarily focused on heteroepitaxial architectures or gallium oxide grown over insulating substrates of the same material. In this work, the activation energies related to point defects in gallium oxide were extracted from temperature-dependent incremental electron beam irradiation experiments to gain insight into the defect landscape and its influence on minority carrier transport and recombination dynamics.