Sequential Redox Precipitation and Solvent Extraction for Comprehensive Metal Recovery from Spent High Manganese Lithium-Ion Battery

The traditional recycling process of spent lithium-ion battery(LIB) with high Mn content faces the defects of high cost of neutralization and precipitation, poor economics of Mn extraction, and serious Li loss. Therefore, this paper introduces a comprehensive hydrometallurgical method for extracting valuable metals from high-Mn spent LIB. Particularly, directional precipitation of Mn was achieved by utilizing its redox properties, and shot-process extraction and enrichment of Li was realized by using the extractant HBL121. In a sulfuric acid system, control of the oxidant dosage to 0.8% resulted in high leaching efficiencies for Li, Ni, Co, and Mn, with values of 96.58%, 96.13%, 95.22%, and 94.24%, respectively, under optimal conditions which were C(H2SO4) of 3.5 mol/L, V(H2O2) of 0.8% (v/v), L/S of 10:1, temperature of 60 °C, and time of 60 min. Subsequently, the addition of KMnO4 dosage (Kp/Kt) in a ratio of 1:1 resulted in the precipitation of 98.47% of Mn as MnO2, with Ni and Li precipitation efficiencies of 0.2% and 0.1%, respectively. Cascade extraction of Ni and Co was reached by using Cyanex272 extractant from the solution after Mn precipitation. At an organic-to-aqueous phase ratio (O/A) of 1:5, the Co extraction efficiency reached 98.68%, whereas the loss efficiency of Ni was 5.53%, and Li was less than 0.1%. Adjusting the O/A to 1:1 increased the Ni extraction efficiency to 89.99% and Li loss to 8.95%. Finally, the HBL121 extractant was utilized to extract Li from the Li-rich solution, achieving 95.08% extraction efficiency. The Li was stripped with 2 mol/L H2SO4 from the load organic phase, realizing a Li concentration of 11.44 g/L. Thus, this process facilitates the comprehensive and efficient recovery of valuable metals such as Li, Ni, Co, and Mn from spent high-Mn LIB.