Performance Study of Biomass Carbon-Based Materials in Electrocatalytic Fenton Degradation of Printing and Dyeing Wastewater

Biomass carbon materials exhibit a significant specific surface area, carbon defects, and oxygen-containing functional groups during the electrochemical cathodic oxygen reduction (ORR) process, resulting in an enhanced adsorption–desorption of reaction intermediates (e.g., *OH and *OOH) by the catalyst. In this study, a cost-effective biomass-derived carbon material (HBC-500) was prepared through low-temperature pyrolysis at 500 °C using Spirulina as a precursor for H2O2 production. By employing surface engineering modification of the carbon-based material to promote the ORR process’s two-electron selectivity, HBC-500 demonstrated consistent experimental results with the RRDE findings at pH = 5, yielding 238.40 mg·L−1 of hydrogen peroxide within a 90 min duration at a current density of 50 mA·cm−2. Furthermore, HBC-500 accomplished over 95% degradation within 30 min at pH = 5 and maintained approximately 91.79% electrocatalytic activity after undergoing five consecutive electrocatalytic cycles lasting 300 min. These results establish HBC-500 biomass carbon material as a highly suitable candidate for H2O2 production and Fenton degradation of organic wastewater.