Sustainable Use of Taveiro (Portugal) Red Clays for Structural Ceramic Applications: Mineralogical and Technological Assessment

The technological potential and sustainability of red clays from the Taveiro region (Coimbra, Portugal) for structural ceramic applications have been investigated. Thirteen representative samples granulometric, mineralogical, chemical analysis, and technological characterization were conducted to determine the suitability for extrusion-based ceramics, aligned with circular economy and climate goals (e.g., PNEC2030, RNC2050). The samples exhibited a high fine fraction content (<0.002 mm up to 76%) and plasticity index (PI; up to 41%), associated with significant smectite, illite, and kaolinite content. Bulk mineralogy was dominated by Σ phyllosilicates (up to 77%) and quartz (12%–29%), while chemical analyses showed high SiO2 and Al2O3 content, moderate Fe2O3, and low CaO/MgO, typical of aluminosilicate clays for red ceramics. High cation exchange capacity (CEC; up to 49 meq/100 g) and specific surface area (SSA; up to 83 m2/g) reflected smectite-rich samples. Firing tests at 900 and 1000 °C demonstrated decreasing water absorption and shrinkage with increased temperature, with some samples yielding lower porosity and higher strength (~12 MPa), confirming suitability for bricks and tiles. Two samples showed higher plasticity but greater shrinkage and porosity, suggesting applicability in porous ceramics or blends. This work highlights the role of mineralogical and technological indicators in guiding the eco-efficient use of georesources for ceramic manufacturing.