Application of equal channel angular pressing improves tensile and yield strength in aluminum alloys, suggesting its potential for lightweight components.
The ECAP (equal channel angular pressing) technique plays a crucial role in enhancing the overall performance of aluminum alloys. In this study, ECAP was applied to a self-developed micro-alloyed Al-0.7Fe-0.4Mg-0.1Si-0.5Er aluminum alloy to investigate the strengthening effects of varying numbers of passes. The results show that after four ECAP passes, the alloy achieved a high tensile strength (208 MPa), yield strength (175.4 MPa), elongation after fracture (10.8%), and a relatively high electrical conductivity (57.1%IACS). The enhanced strength is primarily attributed to precipitation strengthening (σp), grain refinement strengthening (σgbs), and dislocation strengthening (σdis). The grain refinement is a result of dynamic recrystallization (DRX) induced by severe plastic deformation. This study demonstrates that ECAP enables a significant improvement in the mechanical properties (82.3%) of the alloy while causing only a marginal reduction (2.9%) in electrical conductivity. These findings provide both technological and theoretical support for the manufacturing of high-performance conductors and other lightweight electrical structural components.
No takes yet. Share an insight, caveat, or question.
He et al. (2025) studied this question.
Synapse has enriched one closely related paper. Consider it for comparative context: