Influence of Stirring Pin Geometry on Weld Appearance and Microstructure in Wire-Based Friction-Stir Additive Manufacturing of EN AW-6063 Aluminium

Additive manufacturing of metal components is predominantly based on fusion-welding processes involving melting and solidification. However, processing high-strength aluminium alloys presents challenges, including reduced mechanical properties and increased susceptibility to hot cracking. To address these issues, alternative solid-state processing methods for aluminium are being explored worldwide. One such method is wire-based friction-stir additive manufacturing, which builds on the principles of friction-stir welding. This study focused on assessing a range of pin tool designs to promote improved mixing between the filler material and substrate. The best results were achieved using a two-stirring-probe configuration, which was then employed to fabricate a multilayer wall made of EN AW-6063 aluminium alloy. The resulting structure showed significant grain refinement, with the deposited layers having an average grain size approximately four times smaller than that of the substrate, indicating dynamic recrystallisation. Tensile testing of the intermediate layer revealed a strength of 147 MPa and 10% elongation, corresponding to 77% of the filler wire strength. These findings highlight the potential of the W-FSAM process for producing near-net-shape, high-quality lightweight metal components with refined microstructures and reliable mechanical performance.