Synthesis of zeolite LTA from kaolin and its model CBC and WAC performance: Optimized by central composite design

In this study, a cost-effective route to synthesizing LTA-type zeolite from Bal?kesir-region kaolin was demonstrated. Kaolin was calcined at 800?C to obtain metakaolin, which was then treated hydrothermally in the presence of NaOH under optimized conditions determined by a Box-Behnken experimental design. The process variables NaOH concentration, temperature, and solid to liquid ratio were systematically investigated to maximize both water adsorption capacity and cation-exchange capacity (CEC). Quadratic regression models and ANOVA confirmed that NaOH concentration and temperature exert the most significant impact on zeolite formation and performance. Characterization by XRD, SEM, and FTIR confirmed that the synthesized product under optimal conditions predominantly consisted of LTA-type zeolite crystals, as evidenced by the characteristic diffraction peaks, morphology, and vibrational bands. The best performing sample showed a CEC of up to 192 mg CaCO? g?? and a water adsorption capacity of nearly 29 g H?O per 100 g adsorbent. These results highlight the potential of locally sourced kaolin for producing high value zeolites, offering a sustainable alternative to imported raw materials.