Microstructure, Esthetics and Engineering Performance of TiN Coatings Deposited by Multi-Arc Ion Plating

Despite extensive research on the effect of nitrogen flow rate on titanium nitride (TiN) coating properties, its influence on esthetic and engineering performance through microstructure control remains insufficiently explored. To simultaneously meet the requirements for surface strengthening and decorative esthetics in high-end stainless-steel crafts, TiN coatings were deposited on 304L stainless-steel substrates using multi-arc ion plating. The regulatory mechanisms and synergistic evolution laws of nitrogen flow rates (100, 200, and 300 sccm) on the microstructure, decorative properties (color and gloss), and engineering performance (adhesion strength, hardness, wear resistance, and corrosion resistance) of the coatings were investigated. At a nitrogen flow rate of 200 sccm, the coating exhibited a uniform and dense columnar crystal structure, as well as a saturated golden hue with high surface gloss. Additionally, the film–substrate adhesion, microhardness, tribological properties, and corrosion resistance reached optimal levels. In contrast, excessively low (100 sccm) or high (300 sccm) nitrogen flow rates resulted in coarse particles and blurred grain boundaries owing to uncontrolled droplet ejection or target poisoning, respectively, thereby deteriorating both appearance and engineering performance. These findings can inform the optimization of TiN coatings, enabling the design of surfaces that simultaneously meet esthetic and high-performance engineering requirements.