Rotating Bending Fatigue Properties of 30CrNi2Mo Steel After Electropulsing-Assisted Ultrasonic Surface Rolling Process

With the rapid development of mechanical components, increasingly stringent demands are placed on steel properties—particularly tensile strength and rotating bending fatigue resistance. This study systematically investigates the effects of the electropulsing-assisted ultrasonic surface rolling process (EUSRP) on the surface microstructure and fatigue performance of 30CrNi2Mo steel. A fine-grained surface layer (depth: 80 μm) was formed. Lath martensite width decreased significantly from 7 μm to 4 μm after EUSRP treatment, which was significantly refined after electropulsing treatment and an ultrasonic surface-rolling process. Under identical stress amplitudes, the rotating bending fatigue life of EUSRP-treated specimens substantially exceeded that of the as-machined state. Fatigue cracks in the as-machined state consistently initiated at the surface, coalesced, and propagated into large cracks, leading to premature fracture. In EUSRP-treated samples, crack initiation shifted to subsurface regions, delaying failure and extending fatigue life.