An Experimental and Numerical Investigation on Enhancing the Ballistic Resistance of 316L Stainless Steel Plates Against Blunt Projectiles by Covering with 2024-T351 Aluminum Alloy Thin Plates

To improve the ballistic resistance of hydrogen storage tank-grade 316L austenitic stainless steel (ASS) plates that are prone to shear plugging failure under blunt projectile impact, this study proposes a non-bonded bilayer protective configuration: covering the 316L ASS substrate with a thin front layer of 2024-T351 aluminum alloy (AA) plate. Ballistic impact tests were performed on monolithic 5 mm thick 316L ASS plates and bilayer targets composed of a 2.05 mm thick 2024-T351 AA plate and a 5 mm thick 316L ASS substrate (total thickness: 7.05 mm), using a single-stage light gas gun combined with high-speed photography. Parallel explicit dynamics models were established using ABAQUS/Explicit, incorporating a modified Johnson–Cook constitutive model and a Lode-dependent Modified Mohr–Coulomb (MMC) fracture criterion, thereby enabling rigorous mutual validation between experimental results and numerical simulations. Results demonstrate that the addition of a mere 2.05 mm thick aluminum alloy front layer significantly enhances the ballistic limit velocity (BLV) of the 5 mm thick 316L stainless steel target plate, increasing it from 167.5 m/s to 250.7 m/s. The enhancement mechanism is closely related to the transition in the failure mode from localized shear plugging to a combination of bulging, dishing, and plugging. This shift substantially improves the structure’s overall plastic deformation capacity and energy dissipation efficiency. This research provides an effective solution and establishes a reliable experimental–numerical benchmark for the lightweight, impact-resistant design of hydrogen storage tanks.