Nitric Acid Purification of Molybdenite Concentrate: Copper-Iron Removal and Development of a Comprehensive Dissolution Kinetics Model

The selective removal of impurities from molybdenite concentrates is crucial for producing high-purity molybdenum products. In this study, the purification of molybdenite concentrate was investigated using nitric acid as both a leaching medium and oxidizing agent. Leaching experiments were carried out under various conditions of temperature (22–78 °C) and nitric acid concentration (0.12–0.48 M). The results demonstrated that while molybdenite remained mostly undissolved, copper and iron were effectively leached, with near-complete removal at 78 °C in 0.24 M HNO3 after 6 h. Compared with other acid systems, nitric acid leaching experiments in this study demonstrated higher efficiency and selectivity under relatively moderate conditions of concentration and temperature. Kinetic analyses were performed based on the shrinking core model (SCM) and extended by developing a comprehensive rate equation that incorporates both nitric acid concentration and reactive surface effects. Fitting the developed model to experimental data revealed distinct kinetic regimes below and above 50 °C, suggesting a mechanism shift from surface chemical reaction control to diffusion through an ash layer. The purified molybdenite was characterized by SEM-EDS and ICP-OES, confirming almost complete elimination of Cu and Fe impurities. This work highlights nitric acid as a promising and efficient medium for selective leaching of molybdenite concentrates and provides a comprehensive kinetic model applicable across different leaching conditions.