Structure and Properties of Sprayed Polyurethane Bio-Based Foams Produced Under Varying Fabrication Parameters

The influence of both mixing pressure and substrate temperature on the structure and properties of spray polyurethane foams produced with a high content (80%) of tall oil-based polyol was investigated. The use of a renewable feedstock such as tall oil polyol aligns with the principles of sustainable development by reducing the carbon footprint and minimizing the environmental impact of the production process. The research focused on identifying the relationships between process parameters and the resulting materials’ thermal insulation properties, physico-mechanical performance, thermal behavior, cellular structure, and chemical composition. The results demonstrated that increasing the mixing pressure (from 12.5 to 17.5 MPa) and substrate temperature (from 40 to 55 °C) led to a reduction in average pore diameter, an increase in closed-cell content up to 94.5% and improved structural homogeneity. The thermal conductivity coefficient (λ) ranged from 18.55 to 22.30 mW·m−1·K−1 while apparent density varied between 44.0 and 45.5 kg·m−3. Higher mixing pressure positively affected compressive strength, whereas elevated substrate temperature reduced this parameter. Brittleness, water uptake, and dimensional stability remained at favorable levels and showed no significant correlation with processing conditions. These findings confirm the high quality of the materials and highlight their potential as sustainable, environmentally friendly insulation foams.