Frost Resistance of Fully Recycled Coarse Aggregate Concrete in Saline-Soil Regions: Seasonal Freezing

With global sustainable construction growth, fully recycled coarse aggregate concrete (RCAC)—eco-friendly for cutting construction waste and reducing natural aggregate over-exploitation—has poor durability in seasonally freezing saline-soil regions (e.g., Tumushuke, Xinjiang): freeze-thaw and salt ions (NaCl, Na2SO4) cause microcracking, faster performance decline, and shorter service life, limiting its use and requiring better salt freeze resistance. To address this, a field survey of Tumushuke’s saline soil was first conducted to determine local salt type and concentration, based on which a matching 12% NaCl + 4% Na2SO4 mixed salt solution was prepared. RCAC specimens modified with fly ash (FA), silica fume (SF), and polypropylene fiber (PPF) were then fabricated, cured under standard conditions (20 ± 2 °C, ≥95% relative humidity), and subjected to rapid freeze-thaw cycling in the salt solution. Multiple macro-performance and microstructural indicators (appearance, mass loss, relative dynamic elastic modulus (RDEM), porosity, microcracks, and corrosion products) were measured post-cycling. Results showed the mixed salt solution significantly exacerbated RCAC’s freeze-thaw damage, with degradation severity linked to cycle count and admixture dosage. The RCAC modified with 20% FA and 0.9% PPF exhibited optimal salt freeze resistance: after 125 cycles, its RDEM retention reached 75.98% (6.60% higher than the control), mass loss was only 0.28% (67.80% lower than the control), and its durability threshold (RDEM > 60%) extended to 200 cycles. Mechanistic analysis revealed two synergistic effects for improved performance: (1) FA optimized pore structure by filling capillaries, reducing space for pore water freezing and salt penetration; (2) PPF enhanced crack resistance by bridging microcracks, suppressing crack initiation/propagation from freeze-thaw expansion and salt crystallization. A “pore optimization–ion blocking–fiber crack resistance” triple synergistic protection model was proposed, which clarifies admixture-modified RCAC’s salt freeze damage mechanism and provides theoretical/technical guidance for its application in extreme seasonally freezing saline-soil environments.