Thermodynamics of gallium-stabilized delta-plutonium: A high-temperature drop calorimetry study

Throughout the Cold War (1947–1991), both the United States and the former Soviet Union independently derived a phase diagram for the Pu-Ga system that has different implications on Pu phase stability. In the phase diagram produced by the United States, the Pu δ-phase is thermodynamically stable at room temperatures when Ga content is between 2 and 9 at. %. The diagram produced by the Soviet Union shows the δ-phase undergoing an eutectoid decomposition into the α-Pu + α-Pu3Ga at 7.9 at. % Ga and 370 K. This would suggest that Ga-stabilized δ-Pu is metastable with respect to α-Pu + α-Pu3Ga at 298 K. To investigate this, and the thermodynamic behavior of Ga in the FCC lattice of δ-Pu, we have utilized high-temperature drop calorimetry to study the enthalpy of formation of two δ-Pu1−xGax compositions. In doing so, mixing models (regular and subregular) were developed to understand the thermodynamic behavior of Ga in the FCC lattice of δ-Pu and found a strong departure from ideal conditions, which suggests Ga ordering in the FCC lattice of δ-Pu. Overall, it was found that δ-Pu1−xGax is enthalpically metastable with respect to α-Pu + Pu3Ga at 298 K.