Effect of GGBFS Content and Curing Temperature on Early-Age Strength and Maturity-Based Modeling of Concrete

This study investigates the early-age compressive strength development of concrete incorporating ground granulated blast-furnace slag (GGBFS) under varying water-to-binder (W/B) ratios (35%, 45%, and 55%) and curing temperatures (5 °C, 20 °C, and 35 °C). Concrete mixtures were prepared with 0%, 20%, and 40% GGBFS replacement levels, maintaining a constant slump of 180 mm. The influence of GGBFS on fresh properties was evident, as higher GGBFS content reduced the demand for high-performance air-entraining water-reducing admixture (AEWR) by up to 72% at 40% GGBFS and W/B of 35%. All mixtures maintained target air content within 4.5 ± 1.5%. The Nurse–Saul maturity method was applied to determine the datum temperature T0 (The minimum temperature required for the degree of maturity to increase) for early-age strength prediction. The optimal T0 was found to be −3 °C for both OPC and GGBFS-blended concretes, replacing the conventional −10 °C value. Compressive strength predictions were conducted using Plowman, Logistic, and Gompertz models within the 5–10 MPa range. The Plowman and Gompertz models predicted early-age compressive strength with an error of approximately 10% in the 5–10 MPa range. In the lower strength range of 3–5 MPa, the Gompertz model exhibited superior predictive performance, with prediction errors 0.5–1 MPa lower than those obtained using the Plowman model. These findings will help in enhancing the maturity method’s reliability for low-temperature or time-constrained construction and support the use of GGBFS as a sustainable cement replacement. The study offers practical insights into optimizing early-age performance in blended cementitious systems.