Composite nanofibers for tissue engineering applications were prepared with polyvinylidene fluoride and polyvinyl alcohol via a horizontal electrospinning process. The effect of the processing parameters (polymer concentration, voltage, feed rate and tip-to-collector distance) on the fibre diameter was studied using L9 orthogonal arrays of the Taguchi Method, S/N ratio, and ANOVA to produce uniform and finest fibre. The optimum parameters were at 90 wt% PVDF ratios for polymer concentration, applied voltage at 10 kV, feed rate at 0.5 mL/h and tip-to-collector distance at 15 cm. The PVDF/PVA electrospun compromises 171.60 nm nanofiber diameter with homogenous morphology and no bead formed. MTT and live/dead kit assay analysis toward human (HSF) cells confirmed the potential of the PVDF/PVA electrospun to be used as an alternative tissue template to allow new cell or tissue formation in the future.
No takes yet. Share an insight, caveat, or question.
Hamzah et al. (2024) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: