Half‐Metallic Ferromagnetism in 2D Janus Monolayers: Mn₂GeX (X = As, Sb)

Two‐dimensional (2D) Janus materials are a fascinating class of materials resulting from their unique electronic and magnetic properties induced by mirror symmetry breaking. However, 2D Janus materials with intrinsic magnetism remain rather rare, casting a mysterious veil over magnetism. In this work, the electronic and magnetic properties of Janus Mn 2 GeX (X = As, Sb) monolayers using the first‐principles calculations are investigated. The results demonstrate that these Janus materials exhibit excellent mechanical and dynamic stability, indicating their potential for future applications in nanoscale spintronic devices. Interestingly, the Janus and monolayers possess exciting half‐metallic character with wide half‐metallic gaps of 0.29 and 0.18 eV, and spin gaps of 1.68 and 1.62 eV, respectively. Their calculated ground state exhibits a strong preference for ferromagnetic ordering, with a Curie temperature () of 630 and 590 K, respectively. Additionally, the ferromagnetism of Janus Mn 2 GeX (X = As, Sb) monolayers is robust against biaxial strain ranging from −6% to 6%. Under 6% tensile strain, the calculated of the monolayer is 639 K, which represents a 9% increase compared to the observed in the unstrained condition. All these intriguing electronic and magnetic properties make the Janus Mn 2 GeX (X = As, Sb) monolayers an appealing candidate for applications in nanoscale spintronic devices.