Control of wetting and uniformity via ZrSix formation in ceramic‐to‐metal joints fabricated using Ag‐Zr brazes

The deposition of a 2.0 µm SiO 2 film on the alumina surface in Kovar TM /94% alumina joints enables the formation of a silicide reaction layer on the alumina during brazing with 97Ag2Zr1Cu. Additionally, the average and standard deviation of joint thickness decrease from 50 to 15 and 29 to 4 µm, respectively compared to joints without added SiO 2 . Finally, the average failure stress of these braze joints was 45 MPa, while that of similar joints without added SiO 2 was 90 MPa. Sessile drop experiments of 98Ag2Zr on SiO 2 and 99.6% Al 2 O 3 substrates show that the braze wets and spreads to 3x its original area on SiO 2 with a wetting angle near 0°, but remains the same area on 99.6% Al 2 O 3 with a wetting angle of 106.6°. Focused‐ion‐beam scanning electron microscopy analysis of a cross‐section of the 98Ag2Zr sessile drop on the SiO 2 substrate has shown that Zr reacts with SiO 2 to form Zr oxide and silicide layers. Scanning transmission electron microscopy diffraction and energy dispersive X‐ray spectroscopy analysis indicate this silicide layer contains tetragonal Zr 5 Si 4 . Analysis shows the silicide layer enhances wetting and joint uniformity while unreacted SiO 2 embrittles the joint and degrades strength.