Augmenting microstructure and tribological performance of wire arc additive manufactured PH13-8Mo stainless steel via TiC/TiB2 nano-particles incorporation

This study aimed to investigate the effect of TiC and TiB 2 nano-inoculants addition on the microstructure and tribological behavior of PH13-8Mo stainless steel processed through wire arc additive manufacturing (WAAM). The incorporation of TiC/TiB 2 inoculants demonstrated notable efficiency in mitigating the anisotropic wear and scratch response and enhancing wear resistance observed in the as-printed state. This improvement was ascribed to the refinement of the grain structure, disruption of the columnar structure, and increased content of the retained austenite. Notably, TiB 2 inoculation exhibited superior grain refinement and achieved the highest hardness. However, the TiC-inoculated condition demonstrated the best wear resistance, attributed to its excellent combination of hardness and fracture resistance, and a higher contribution of strain-induced martensite transformation during wear testing. Additionally, the implementation of post-printing solutionizing and aging treatment was found to improve the scratch and wear resistance of the alloy, attributed to the formation of nano-sized β-NiAl precipitates. The main wear mechanism observed involved oxidation wear, adhesive wear, and three-body abrasive wear. The findings of this study highlight the significant potential of incorporating ceramic-based nano-particles for improving the wear resistance of WAAM PH13-8Mo components, particularly in demanding applications like injection molding dies where superior abrasion resistance is paramount.