Hydroxyapatite coating of TiNi shape memory alloy via Electrophoretic Deposition (EPD)

In this study, hydroxyl apatite (HA) as a bio-ceramic is coated on the TiNi shape memory. In this approach, Tri-ethanolamine and butanol were used as suspensions. To set up Electrophoretic Deposition (EPD) process, voltages of 20, 30 and 40 volts were applied on the cathode for 1-5 minutes. The sintering process was done in the Ar atmosphere for two hours at 800°C. SEM and XRD were used to investigate surface morphologies and phases. Obtained results showed that higher electrical currents led to generation of thicker coatings registering 105% and 12.3% improvement for weight and thickness after 6 minutes, respectively. Moreover, Transformation of HA to other calcium phosphate phases doesn't happen at a sintering temperature of 800°C. Moreover, a uniform, homogeneous and crackles coating can be reached in the voltage of 30 volts at low sintering temperatures. This process can be utilized an alternative technique for bioactive coatings.