Preparation of Al@FTCS/P(VDF-HFP) Composite Energetic Materials and Their Reaction Properties

Strengthening the interfacial contact between the reactive components effectively boosts the energy release of energetic materials. In this study, we aimed to create a close-knit interfacial contact condition between aluminum nanoparticles (Al NPs) and Polyvinylidene fluoride-hexafluoropropylene (P(VDF-HFP)) through hydrolytic adsorption and assembling 1H, 1H, 2H, 2H-Perfluorododecyltrichlorosilane (FTCS) on the surface of Al NPs. Leveraging hydrogen bonding between -CF and -CH and the interaction between C-F⋯F-C groups, the adsorbed FTCS directly leads to the growth of the P(VDF-HFP) coating layer around the treated Al NPs, yielding Al@FTCS/P(VDF-HFP) energetic composites. In comparison with the ultrasonically processed Al/P(VDF-HFP) mixture, thermal analysis reveals that Al@FTCS/P(VDF-HFP) exhibits a 57 °C lower reaction onset temperature and a 1646 J/g increase in heat release. Associated combustion tests demonstrate a 52% shorter ignition delay, 62% shorter combustion time, and a 288% faster pressurization rate. These improvements in energetic characteristics stem from the reactivity activation of FTCS towards Al NPs by the etching effect to the surface Al