Electron microscopy characterization of proton irradiation induced growth in pure Zr

Irradiation induced growth is a constant volume shape change that occurs without externally applied stress that is observed in some materials under irradiation damage. Proton irradiation was carried out on a pure Zr sample to many dpa, to enable investigation of microscale aspects of the irradiation growth phenomenon. Irradiation induced a significant surface morphology change in the irradiated area, which is believed to be the result of the anisotropic growth behavior of the hcp structured Zr. The localized strain that developed was characterized by Electron back scatter diffraction (EBSD), on both the irradiated surface and on a cross sectional through-thickness plane. It was found that there is a correlation between the amount of local deformation and level of misorientation existing between two adjacent grains. The irradiation induced defect microstructure was characterized by transmission electron microscopy (TEM), showing and <c> component loops similar to that generated by neutron irradiation in literature. Lastly, site specific focused ion beam (FIB) TEM lift-outs were prepared on local grain boundaries to investigate the origin of the localised deformation.