Carburisation and melting of hot compacted iron in a coke bed

One of the key technologies in developing hydrogen-enriched ironmaking operations is the control of the carburisation, melting, and dripping behaviour of the iron ore burden materials. When a hot compacted iron (HCI) is charged in the blast furnace or the FINEX Melter-Gasifier, iron oxide reduction, the reduced iron’s carburisation, and the melting of iron and slag occur successively. This study investigated the reduction, carburisation, melting and dripping behaviour of HCI under a CO-H2 gas mixture using the high-temperature X-ray radiographic technique. Under 100 per cent CO gas atmosphere, the dripping temperature was 1410°C. When 5 per cent H2 was introduced, the dripping temperature slightly decreased to 1400°C. Furthermore, the dripping temperature gradually increased as the H2 gas composition increased. As 30 per cent H2 was introduced, the dripping temperature reached 1414°C. The carbon concentration in the drained metal samples gradually increased with increasing H2 composition. It is considered that H2 decreased FeO content in the slag, yielding the increased melting temperature and viscosity of the slag. On the other hand, H2 accelerated the carburisation of the reduced iron by CO gas, enabling the homogenisation of the oxide materials to form a liquid phase. Therefore, it is considered that introducing H2 in the reactor is helpful to increase productivity and energy efficiency by accelerating the liquid phase’s formation.