In this paper glass crystallization behavior of 50ZnO:47B2O3:3Nb2O3:0.5Eu2O3 (G-0h) glass has been investigated in detail by DSC, XRD and TEM analysis. The luminescent properties of resulted glass-ceramics were also investigated. By XRD and TEM analysis crystallization of several crystalline phases have been proved (α-Zn3B2O6, β-Zn3B2O6 and ZnNb2O6). By calculating of crystal parameters it was found that europium ions are successfully incorporated in the β-Zn3B2O6. Photo-luminescent spectra show an increased emission in the resulting glass-ceramic samples as compared with the parent glass sample because of the higher asymmetry of Eu3+ ions in the crystalline phases obtained. It was established that the optimum emission intensity is registered for glass-ceramic sample obtained after 25 hours heat treatment of the parent glass.