The synthesis of mesoporous material by utilizing palm oil boiler ash (POBA) waste as the silica source and methyl ester sulfonate (MES) surfactant as the template for a high-porosity was investigated for free fatty acids (FFA) adsorption. The research was initiated with silica extraction from POBA by sodium hydroxide addition through the sol-gel precipitation method. Silica modification was carried out with MES surfactant and 3-aminopropyltrimethoxysilane (APTMS) as the co-structure-directing agent (CSDA) in different calcination temperatures. Mesoporous silica-POBA (MS-POBA) free template had a surface area, pore diameter, and pore volume (41.033 m2/g, 4.180 nm, and 0.250 cm3/g) lower than MS-POBA with the template (71.0147 m2/g, 7.923 nm, and 0.524 cm3/g). The ability of MS-POBA to adsorb FFA reached its optimum conditions with an adsorption time of 20 min and an adsorbent dosage of 0.24 g. The FFA removal by MS-POBA with the template was found to have higher adsorption ability, which was 35.54%, compared to the MS-POBA free template of 26.68%. The high porosity of MS-POBA with a template makes the FFA adsorption capacity of this material higher than MS-POBA free template.
Sitohang et al. (Sat,) studied this question.