Preparation and Properties of Bilayer Composite Materials of Cu-coated Fe and CuSn10

Bilayer composite materials of Cu-coated Fe and CuSn10 containing 0%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50% Cu-coated Fe were prepared in mesh belt sintering furnace. Microscopic pore morphology of materials was observed, bending strength was tested. Results show that, There is a good bonding between Cu-coated Fe and CuSn10, with the increase of Cu-coated Fe content from 0% to 50%, bending strength of bilayer composite materials increases.