Elastic Properties of Low-Dimensional Single-Crystalline Dielectric Oxides through Controlled Large-Area Wrinkle Generation

Freestanding single-crystalline SrTiO3 membranes, as high-κ dielectrics, hold significant promise as the gate dielectric in two-dimensional (2D) flexible electronics. Nevertheless, the mechanical properties of the SrTiO3 membranes, such as elasticity, remain a critical piece of the puzzle to adequately address the viability of their applications in flexible devices. Here, we report statistical analysis on plane-strain effective Young's modulus of large-area SrTiO3 membranes (5 × 5 mm2) over a series of thicknesses (from 6.5 to 32.2 nm), taking advantage of a highly efficient buckling-based method, which reveals its evident thickness-dependent behavior ranging from 46.01 to 227.17 GPa. Based on microscopic and theoretical results, we elucidate these thickness-dependent behaviors and statistical data deviation with a bilayer model, which consists of a surface layer and a bulk-like layer. The analytical results show that the ∼3.1 nm surface layer has a significant elastic softening compared to the bulk-like layer, while the extracted modulus of the bulk-like layer shows a variation of ∼40 GPa. This variation is considered as a combined contribution from oxygen deficiency presenting in SrTiO3 membranes, and the alignment between applied strain and the crystal orientation. Upon comparison of the extracted elastic properties and electrostatic control capability to those of other typical gate dielectrics, the superior performance of single-crystalline SrTiO3 membranes has been revealed in the context of flexible gate dielectrics, indicating the significant potential of their application in high-performance flexible 2D electronics.