High-Pressure Structural and Optical Studies of Pure Low-Dimensional Cesium Lead Chlorides CsPb₂Cl₅ and Cs₄PbCl₆

We report high-pressure single-crystal X-ray diffraction, optical absorption, and photoluminescence investigations of all-inorganic perovskite-related materials CsPb2Cl5 and Cs4PbCl6. The crystal structure of CsPb2Cl5, composed of alternate layers of Cs+ cations and Pb–Cl frameworks, is stable under pressure up to at least 4.2 GPa. Because external stress is mainly absorbed by the Cs+ layers, the optical absorption edge of the crystal only slightly red-shifts with increasing pressure, which correlates well with a moderate shortening of the Pb–Cl bonds. A quite different response to pressure shows Cs4PbCl6, the crystal built of isolated PbCl64– octahedra and Cs+ cations. During the compression at around 3.4 GPa, the trigonal phase I, space group R3̅c, transforms to the orthorhombic phase II, space group Cmce, which at around 4 GPa transforms into phase III. On decompression, phase II is not restored, but phase III converts through a diffuse phase transition into another high-pressure phase IV, which is stable in a wide pressure range and transforms to the initial phase I only around atmospheric pressure. The red shift of the absorption edge and the profound modification of the absorption spectrum in phase II were ascribed to the deformation of the PbCl64– octahedra. The transition to phase III induces a blue shift of the absorption edge, while the transition to phase IV is associated with a large red shift. Photoluminescence was detected in phases I and II with the intensity quenched with increasing pressure.