Electrochemical formation of Pr aided by additive (KF) in LiCl-KCl molten salt

In order to investigate the influences of the additive (KF) on electrochemistry and deposit morphology of Pr, various electrochemical techniques were used to comparative investigate the electroreduction potential and diffusion coefficient of Pr 3+ and kinetic properties of Pr 3+ /Pr in LiCl-KCl-PrCl 3 before and after the addition of KF at different molar concentration ratio of F − to Pr 3+ ( k ). Cyclic voltammetry, square wave voltammetry and reverse chronopotentiometry results showed that the value of k ( k = 0, 1, 2, 3 and 4) had no effect on reduction mechanism of Pr 3+ . With the increase of k , the reduction peak potential moved in the negative direction, the diffusion coefficient decreased, and diffusion activate energy increased. Meanwhile, the exchanged current densities ( j 0 ), charge transfer resistances ( R ct ), and activate energies ( E a ) were measured at different k by linear polarization technique, which illustrated that with the augment of k , j 0 gradually reduced, and E a and R ct increased. Furthermore, the electrochemical preparation of Pr aided by KF was explored by potentiostatic electrolysis at different k , and the products were characterized by XRD, SEM and EDS, which indicated that with the increase of k , the morphology of metallic Pr changed from slender needles to granular.