Super duplex stainless steel (SDSS) is a type of stainless steel made of chromium (Cr), nickel (Ni), and iron (Fe). In the present work, a 1.6 mm wide thin sheet of SDSS is joined using gas tungsten arc welding (GTAW). The ideal parameter for a bead-on-plate trial is found, and 0.216 kJ/mm of heat input is used for welding. As an outcome of the welding heating cycle and subsequent cooling, a microstructural study revealed coarse microstructure in the heat-affected zone and weld zone. The corrosion rate for welded joints is 9.3% higher than the base metal rate. Following the corrosion test, scanning electron microscope (SEM) analysis revealed that the welded joint’s oxide development generated a larger corrosive attack on the weld surface than the base metal surface. The percentages of chromium (12.5%) and molybdenum (24%) in the welded joints are less than those in the base metal of SDSS, as per energy dispersive X-ray (EDX) analysis. Corrosion modeling is done using the COMSOL Multiphysics software. Electrochemical corrosion modeling is used to determine the electrolyte potential (i.e., 0.09 V) and current density (i.e., 0.2 A/m² to 1.8 A/m²). An entire mesh model contains 6240 elements. The largest and smallest element sizes are 4 mm and 0.1 mm, respectively. The maximum element rate of growth is 1.2.
No takes yet. Share an insight, caveat, or question.
Kumar et al. (2024) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: