Exploring Phase and Bandgap Variations in Gallium Oxide Using Mist-based Chemical Vapor Deposition System

The present research demonstrates a thermally stable Kappa-phase Gallium Oxide (K-Ga <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> ) using an affordable Mist Chemical Vapor deposition system (MIST-CVD). A systematic growth approach has been used, which shows that the K-Ga <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> is stable at high temperatures with other polymorphs of the Ga <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> family on Sapphire Substrate. Further, the structural, morphological, and optical properties of Ga <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> films have been investigated using XRD, FE-SEM, EDAX, UV-Vis, and Raman measurements.