Experimental analysis demonstrates refined carbide spacing and morphological transitions in high-Cr white irons, highlighting processing routes for in-situ composites.
The effects of chemical composition and solidification rate on the solidification behavior of high-Cr white irons were investigated through directional solidification. Increasing the solidification rate in hypoeutectic alloys caused finer dendrite-arm spacing, as expected. The eutectic structure, which formed in the interdendritic region, was comprised of M7C3 and austenite; however, secondary dendrite arms of hypoeutectic alloys contained a few M7C3 particles that solidified prior to the eutectic structure. The transition from cellular to dendritic solidification occurred at a solidification rate between 50 µm/s and 100 µm/s in a near-eutectic alloy. In the near-eutectic alloy with cellular solidification, a directionally arrayed in-situ composite of M7C3/austenite formed within the cell. Speckle-like features appeared in the intercellular region due to M23C6 carbide precipitation during subsequent cooling after freezing. Like dendrite-arm spacing in hypoeutectic alloys, the inter-speckle spacing and the inter-fiber spacing became finer with an increasing solidification rate in the cellular solidification range.
No takes yet. Share an insight, caveat, or question.
Son et al. (2024) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: