Mössbauer and magnetic studies of Fe-doped ZnO nanoparticles prepared by solution co-precipitation method

A series of Zn[Formula: see text]Fe x O ([Formula: see text], 0.015, 0.045, 0.075) nanoparticles were synthesized using the solution co-precipitation method, and their structural and property characteristics were investigated. X-ray diffraction (XRD) analysis revealed that all Zn[Formula: see text]Fe x O samples exhibited a hexagonal wurtzite crystal structure with the P63mc space group. The introduction of Fe doping led to a slight lattice distortion in the samples. The morphology of the nanoparticles, including polydispersion and agglomeration, as well as the presence of the second phase ZnFe 2 O 4 , was examined by scanning electron microscope (SEM) and transmission electron microscope (TEM). UV–Vis diffuse reflectance spectroscopy demonstrated that the band gap of Zn[Formula: see text]Fe x O lies between 3.152 and 3.163[Formula: see text]eV. With the increase in Fe ion doping, the band gap shows a slight decreasing trend. Mössbauer spectroscopy revealed that iron ions in the nanoparticles existed in a trivalent state and exhibited two different configurations: One involved iron replacing zinc without creating a vacancy, while the other involved iron substituting zinc with a vacancy. The ferromagnetic nature of the Fe-doped samples can be attributed to the exchange interaction between two Fe[Formula: see text] ions mediated by the F-center mechanism.