Sn-Cu-Ni lead-free solder alloy electrodeposited on copper substrate from a deep eutectic solvent (DES)-based electrolyte under direct current (DC) and pulsed current (PC) was subjected to a reflowing process at the industrial company MIBATRON S.R.L. (Otopeni, Romania). The alteration of the alloy’s composition and anti-corrosive properties upon exposure to the reflow process were investigated via Scanning Electron Microscopy (SEM-EDX), X-ray diffraction (XRD), linear sweep voltammetry (LSV) and electrochemical impedance spectroscopy (EIS). Corrosion studies conducted in sodium chloride solution revealed that the system obtained under the DC plating mode (Sn-Cu-Ni-DC) exhibited enhanced anti-corrosive properties compared to the system obtained under PC (Sn-Cu-Ni-PC) after reflowing. However, prior to reflowing, the opposite effect was observed, with Sn-Cu-Ni-PC showing improved anti-corrosive properties. These changes in anti-corrosive behavior were attributed to the modification of the alloy’s composition during the reflowing process.
No takes yet. Share an insight, caveat, or question.
State et al. (2024) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: