Surface Engineering of Enamel with Sodium Hypochlorite: Effects on Bond Strength and Etching Microstructure in Adhesive Applications

Background: Adhesion to enamel is influenced by surface preparation, which affects the micromechanical retention of resin-based materials. Sodium hypochlorite (NaOCl) deproteinization has been proposed as a pretreatment to improve acid etching efficacy, but the optimal application time remains unclear. Methods: This in vitro study evaluated the effect of 5% NaOCl pretreatment at three exposure times (15, 30, and 60 s) on shear bond strength (SBS), the adhesive remnant index (ARI), and enamel etching patterns. Extracted human premolars (n = 140) were divided into four groups: the control (acid etching only) and three experimental groups. SBS was tested per ISO 11405, while ARI scores were assessed under stereomicroscopy, and surface morphology was examined by scanning electron microscopy (SEM). Results: The 30-s NaOCl group exhibited the highest SBS (20.9 MPa) compared with the control (15.9 MPa, p < 0.05) and 15-s (14.9 MPa, p < 0.05) groups. SEM analysis showed predominantly Type I–II etching patterns for the 30-s group, irregular Type III for 15 s, and overetched Type IV with loss of prism definition for 60 s, compromising the adhesive interface. ARI scores indicated 86.7% of samples in the 30-s group retained all adhesive on enamel (score 3). Conclusions: A 30-s 5% NaOCl pretreatment before acid etching improved enamel micromorphology and bonding performance compared to shorter or longer exposures. The intermediate duration provided effective deproteinization without structural damage, whereas prolonged exposure degraded the enamel microstructure. This protocol may offer a simple, cost-effective method to enhance clinical adhesive procedures, though prolonged exposure (60 s) should be avoided due to structural degradation of the enamel microstructure.