The Effect of HiPIMS Pulse Conditions on the Microstructural, Mechanical, and Tribological Properties of TiB2 Coatings on Steel Substrates

This study examines the impact of varying pulse conditions on the properties of titanium diboride (TiB2) coatings deposited by high-power impulse magnetron sputtering (HiPIMS). The coatings were prepared on steel substrates using an industrial-scale system. During the experiments, the HiPIMS frequency and pulse width were systematically varied to examine their influence on the coating’s microstructural, mechanical, and tribological properties. The obtained results show a correlation between process parameters and coating performance. A maximum hardness of 39.7 GPa and a coefficient of friction (CoF) as low as 0.68 were achieved. The best combination of mechanical properties was observed for coatings prepared in a frequency range of 600–1000 Hz and with a pulse width of 50 µs. Notably, the optimal tribological properties and surface roughness were obtained at 800 Hz and a 50 µs pulse width. This work demonstrates that fine-tuning HiPIMS pulse conditions is crucial for achieving high-quality TiB2 coatings with enhanced functional performance.